YSHIELD® TEC54 | Carbon coating | 5 Liter
Carbon coating for technical application procedures. With the 5 µm pigmentation for screen printing, spraying, airless, scraper-, roller-, flow- coating.
Screening attenuation: The indicated dB-values apply to 1/40 GHz. Measurement from 40/600 MHz to 40 GHz according to standards ASTM D4935-10 or IEEE Std 299-2006, view report below.
PDF: Report screening attenuation
Content: 5 liter
Weight: 7200 g
ID: 394 / 1367
Packaging: 230x230x250 mm
Our carbon coatings based on graphite are electrically highly conductive base coatings for a wide range of technical application areas. Application with screen printing, spraying, airless, scraper-, roller-, flow- coating. They are suitable for shielding plastic parts, electrical installation sockets, plastic films, dry construction boards, devices, facilities, etc. or to coat absorber materials, pressure sensors, etc.. In comparison to metal.based shielding varnishes, our products are based on water only, have less than 0.2 g/l VOC, do not contain plasticizers or film building agents and are therefore maximally ecological. All coatings are highly abrasion-resistant, despite the graphite. They have an excellent adhesion to all polar plastic substrates.
Water, natural graphite, pure acrylics dispersion, carbon black, additives, preservative (BIT, INN, MIT).
- Resistance: 3.5 Ohm/square at a coverage of 7.5 qm/l
- Pigmentation size: 5 µm
- Adhesive tensile strength: 8.4 N/mm²
- VOC content: 0.18 g/l
- Viscosity: 2000 mPas
- Sd-value: 0.1 m
- PH-value: 8
- Density: 1.11 kg/l
- Processing temperature: > 10°C
- Container size: 5 Liter
- Shelf life: 12 months
As shielding coating
Screening attenuation at 1 GHz: Single layer 30 dB | Double layer 38 dB | Three layer 46 dB
Screening attenuation at 40 GHz: Single layer 31 dB | Double layer 41 dB | Three layer 50 dB
As technical coating
Electrical resistance: Wet film 200 µm: ~2,5 Ω/ | Wet film 150 µm: ~3,5 Ω/ | Wet film 100 µm: ~7 Ω/
Measured with Schütz-Messtechnik MR-1 and 4-point-probe.
To adjust the resistance or the viscosity please find our additives POLY5 and VISC5 below.